擠出吹塑ABS/錦湖日麗/720V 高硬度 抗靜電 ABS塑料
產(chǎn)品參數(shù)
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
基本性能 | 熔體流動(dòng)速率 | 200℃/5kg | ASTM D-1238 | 4.2 | g/10min |
物理性能 | 比重 | ASTM D-792 | 1.04 | g/cm3 | |
模具收縮率 | Flow | ASTM D-955 | 0.40-0.70 | % | |
機(jī)械性能 | 拉伸屈服強(qiáng)度 | ASTM D-638 | 53.8 | MPa | |
拉伸屈服伸長(zhǎng)率 | ASTM D-638 | 20 | % | ||
彎曲模量 | ASTM D-790 | 2550 | MPa | ||
彎曲屈服強(qiáng)度 | ASTM D-790 | 71.7 | MPa | ||
IZOD缺口沖擊強(qiáng)度 | 23℃,3.18mm | ASTM D-256 | 176 | J/m | |
IZOD缺口沖擊強(qiáng)度 | 23℃,6.35mm | ASTM D-256 | 139 | J/m | |
洛氏硬度 | ASTM D-785 | 115 | R scale | ||
電氣性能 | 體積電阻率 | ASTM D-257 | 1.0E+12 | ohm.cm | |
熱性能 | 熱變形溫度 | 1.80MPa,未退火 | ASTM D-648 | 87.2 | ℃ |
維卡軟化溫度 | ASTM D-1525 | 97.8 | ℃ | ||
燃燒性 | 1.65mm | UL 94 | HB | ||
燃燒性 | 3.18mm | UL 94 | HB |